RUST-CONVERTING RED PRIMER

formulation and technical data sheet for a product named "WBACRY700RF1," which is a protective rust-converting clear-coating. The document details the ingredients and the manufacturing process required to create the coating, as well as specifications for its application and performance. Here's a breakdown of the information:

Formulation

Product Name:

• WBACRY700RF1

Type:

• Protective Rust Converting Clear-Coating

Manufacturing Instructions

STEP 1:

• Mix the following ingredients separately while stirring, and set aside:
  • AMP90 - Neutralizer (Supplier: ANGUS)
  • ASCONIUM-114 - Anticorrosion Additive (Supplier: ASCOTEC)

STEP 2:

• Into the let-down tank, add the following ingredients in order, progressively, with continuous stirring:
  • AC2403 - Binder (Supplier: ALBERDINGK BOLEY)
  • BYK024 - Defoamer (Supplier: BYK)
  • Add the mixture from STEP-1
  • Water
  • ENHANCER 300 - Co-solvent (Supplier: EASTMAN)
  • ACRYSOL RM5000 - Thickener (Supplier: DOW)
  • TEGOWET KL 245 - Wetting Agent (Supplier: EVONIK)
  • ASCOTRAN-H10 - Flash-rust Inhibitor (Supplier: ASCOTEC)
  • ASCOTRUST X1 - Rust Converter (Supplier: ASCOTEC)

Dry Film Thickness (DFT) Variations

• DFT 20µm
• DFT 25µm
• DFT 30µm
• DFT 50µm

Salt-Spray Performances – 250 Hours

Testing Results:

• Indicates that the coating provides protective rust-converting properties.

Coating Types

• Clear-Coating WB Coating
• WB Metal Coating

Various Pre-treatments

• WBACRY700RF1 with Tannic Acid Based Pretreatment
• WBACRY700RF1 with ASCOTRUST Based Pretreatment

Purpose

The document provides comprehensive details for manufacturers and users to evaluate the clear-coating's performance and suitability for various applications. It emphasizes the necessity for full-scale testing in real-world conditions to ensure the product's effectiveness and reliability.

This formulation is intended for creating a water-based, clear coating that converts rust and protects metal surfaces from further corrosion, with various options for dry film thickness and pre-treatment methods.